Vcoat

AA.C 20.0 micron

CLEAR BOPP FILM BOTH SIDES ACRYLIC COATED

Properties

  • Good aroma barrier
  • Excellent hot tack and seal strength
  • Printable on both sides
  • Outstanding optical properties
  • Bisphenol free
  • Improved barrier to mineral oil migration compared to uncoated BOPP

 

Typical Applications

This film is designed for use on HFFS, VFFS & OW applications

 


Business Segment
Flexible  Flexible
Category
Coated  Coated
Features
Aroma Barrier  Aroma Barrier
Bisphenol Free  Bisphenol Free
Food Contact  Food Contact
High Speed  High Speed
Mineral Oil Barrier (MOH barrier)  Mineral Oil Barrier (MOH barrier)
Transparent  Transparent

Properties

Total thickness micron
20.000 micron

Grammage
18.400 g/m²

Yield
54.350 m²/kg

Density
0.920 g/cm³

Test method 1
DIN EN ISO 2286 1-2-3

Appearance
Trasparent


Tensile properties

Tensile strength MD
170.000 N/mm²

Tensile strength TD
280.000 N/mm²

Elongation MD
220.000 %

Elongation TD
80.000 %

Secant Modulus 100%
110 N/mm²

Elastic Modulus 1%
1900.000 N/mm²

Test method 2
ASTM D 882 DIN EN ISO 527 1-3


Optical properties

Gloss 45°
88.000 Gloss unit

Test method 3
ASTM D 2457

Haze
1.400 %

Test method 4
ASTM D 1003


Thermal Stability

Shrinkage MD (hot air 130°C - 5')
4.000 %

Shrinkage TD (hot air 130°C - 5')
2.000 %

Test method 7
OPMA TC4a


Sealing Properties

Sealing Threshold Acr/Acr
~ 90

Seal Strenght 130°C Acr / Acr
>=200

Test method 8
OPMA TC4b


Coefficient of friction

COF Acr / Acr
0.250

COF Acr/met
0.200

Test method 9
ASTM D 1894 - DIN EN ISO 8295-04


Permeability

Oxygen transmission rate (23°C-0%R.H.)
950 cc/(m² d atm)

Test method 10
ASTM D 3985

Water vapor Transmission Rate (37,8°C-90% R.H.)
5,5 g/(m² d)

Test method 11
ASTM F 1249

Water vapor Transmission Rate (23°C-85% R.H.)
1.200 g/(m² d)

Test method 12
DIN 53122