AA.C 40.0 micron

CLEAR BOPP FILM BOTH SIDES ACRYLIC COATED

Properties

  • Good aroma barrier
  • Excellent hot tack and seal strength
  • Printable on both sides
  • Outstanding optical properties
  • Bisphenol free
  • Improved barrier to mineral oil migration compared to uncoated BOPP

 

Typical Applications

This film is designed for use on HFFS, VFFS & OW applications

 

Business Segment
Flexible  Flexible
Category
Coated  Coated
Features
Aroma Barrier  Aroma Barrier
Bisphenol Free  Bisphenol Free
Food Contact  Food Contact
High Speed  High Speed
Mineral Oil Barrier (MOH barrier)  Mineral Oil Barrier (MOH barrier)
Transparent  Transparent

Properties

Total thickness micron
40 micron
Grammage
36.800 g/m²
Yield
27.170 m²/kg
Density
0.920 g/cm³
Test method 1
DIN EN ISO 2286 1-2-3
Appearance
Trasparent

Tensile properties

Tensile strength MD
170.000 N/mm²
Tensile strength TD
280.000 N/mm²
Elongation MD
220.000 %
Elongation TD
80.000 %
Secant Modulus 100%
110 N/mm²
Elastic Modulus 1%
1900.000 N/mm²
Test method 2
ASTM D 882 DIN EN ISO 527 1-3

Optical properties

Gloss 45°
88.000 Gloss unit
Test method 3
ASTM D 2457
Haze
1.900 %
Test method 4
ASTM D 1003

Thermal Stability

Shrinkage MD (hot air 130°C - 5')
4.000 %
Shrinkage TD (hot air 130°C - 5')
2.000 %
Test method 7
OPMA TC4a

Sealing Properties

Sealing Threshold Acr/Acr
~ 90
Seal Strenght 130°C Acr / Acr
>=200
Test method 8
OPMA TC4b

Coefficient of friction

COF Acr / Acr
0.250
COF Acr/met
0.200
Test method 9
ASTM D 1894 - DIN EN ISO 8295-04

Permeability

Oxygen transmission rate (23°C-0%R.H.)
600 cc/(m² d atm)
Test method 10
ASTM D 3985
Water vapor Transmission Rate (37,8°C-90% R.H.)
3,5 g/(m² d)
Test method 11
ASTM F 1249
Water vapor Transmission Rate (23°C-85% R.H.)
0.600 g/(m² d)
Test method 12
DIN 53122